Solder & Solder paste

Classic solder for working with a hand soldering iron. In the center of the solder is a solder paste that simultaneously cleans the surface on which it is soldered and allows better adhesion of the solder. This solder is the so-called leaded.

• Quantity: 50g
• Diameter: 1.0mm
• Composition: Sn60Pb40

Solder paste is used during SMT production, i.e. when SMT components are used. The paste is placed in specific places where it’s desired to achieve a solder joint, either by hand or with a stencil. After that, the components are placed and soldered in special ovens. This paste does not require cleaning after soldering (no clean). Paste is lead-free, which means it does not contain lead.

• Composition: Sn96,5Ag3Cu0,5
• Melting point: 252°C
• Solder ball sizes: 25-45µm
• Packaging: 1.4mL
• Lead-free
• No clean

At e-radionica.com solder paste is stored in the refrigerator, at a temperature of 8 ° C, which is the recommended storage temperature. We recommend that you choose express delivery for orders that contain this item in order to avoid product being exposed to high temperatures.

Solder paste is used during SMT production, i.e. when SMT components are used. The paste is placed in specific places where it’s desired to achieve a solder joint, either by hand or with a stencil. After that, the components are placed and soldered in special ovens. This paste does not require cleaning after soldering and has a low melting point.

• Composition: Sn62Pb36Ag2
• Melting point: 198°C
• Solder ball sizes: 25-45µm
• Packaging: 1.4mL
• Lead based
• No clean

At e-radionica.com solder paste is stored in the refrigerator, at a temperature of 8 ° C, which is the recommended storage temperature. We recommend that you choose express delivery for orders that contain this item in order to avoid product being exposed to high temperatures.

Classic solder for working with a hand soldering iron. Solder paste is in the center of the solder, which simultaneously cleans the surface on which its soldering and gives a better grip of solder.